大学英语词汇短语释义解析及例句 cleavage fracture
释义：
cleavage fracture [力] 解理断裂；可裂性破坏
例句：
The rupture is brittle cleavage fracture.
此属于解理和准解理脆性断裂。
The thermal fatigue fracture belongs to cleavage fracture.
热疲劳断口具有穿晶解理特征。
Crystalline fining grain can restrain the cleavage fracture.
细化晶粒可抑制脆性断裂。
Local cleavage fracture might happen in the front of crack tip.
裂尖前方可能发生形变孪晶，裂纹沿孪晶界扩展。
Dimensions of the stress and crystalline have influence on cleavage fracture.
应力的大小和晶粒的尺寸影响解理断裂。
Transgranular cleavage fracture is shown for the charged layer in tensile specimen.
拉伸试样表面充氢层的断口是穿晶解理断口。
The fractures of the alloys change from dimple to cleavage fracture with river pattern.
合金的断口形貌由韧窝向河流花纹状的解理形貌转变。
The local cleavage fracture stress is mainly determined by the length of the critical microcrack.
细观解理断裂应力主要由临界裂纹的长度决定。
Studies indicate that fracture of cast irons is different from brittle cleavage fracture of steels.
研究结果表明，铸铁的断裂与钢的脆性解理断裂不同。
The results by SEM results show that AZ91D alloy by addition rare earth elements possess the features of quasi-cleavage fracture.
扫描电镜分析结果显示添加稀土的镁合金疲劳断口呈现出准解理断裂特征。
The cleavage fracture of the notched specimens with various sizes and widths is mainly controlled by the criterion of normal stress.
不同尺寸和宽度的缺口试样的解理断裂主要由正应力判据控制。
The fracture morphology was the synthesis of the cleavage brittle fracture (macroscopic) and the accurate cleavage fracture (microscopic).
其断口形貌为解理脆性断裂(宏观)和准解理断裂(微观)的综合。
The cutting tool was characterized by intercrystalline fracture attributed to fatigue and partial cleavage fracture in the machining process.
聚晶金刚石刀具在加工过程中的磨损机理主要表现为具有疲劳磨损特征的沿晶断裂及局部解理断裂。
In the neighbourhood of the unhealed porosities the alloy matrix appeared to be embrittled and in certain cases cleavage fracture was observed.
未锻合疏松周围的合金基体有一定变脆倾向，有时可以观察到解理断口。
Fractographic observations showed that hydrogen could induce surface cracks for smooth specimens and a cleavage fracture pattern for notch specimens at RT.
破断面观察结果显示，在室温中，氢气会导致平滑试片在表面形成裂纹，而在凹槽试片中产生劈裂破坏形态。
According to analysis result of tubes' cracks fracture observation, it proves that the fracture is quasi-cleavage fracture which is characterized by river pattern.
通过对管束大量电子断口的观察分析，证明了断口为准解理断裂，具有河流花样的特征。
The critical event for cleavage fracture in notched specimens is the propagation of a ferrite grain-sized crack into the matrix, and is independent of specimen sizes and widths.
在缺口试样中，解理断裂的临界事件是铁素体晶粒尺寸的裂纹扩展进入基体，不随试样尺寸和宽度变化。
Cleavage fracture is a typical brittle fracture and also a process consisted of crack producing and spreading, and the mechanism is related to dislocation and crystalline grain.
解理断裂是典型的脆性断裂，解理断裂也是一个裂纹萌生和扩展的过程，其机制与位错和晶粒有关。