大学英语词汇短语释义解析及例句 cement paste
释义：
cement paste [建] 水泥浆
例句：
The interface of the cement paste and aggregate is the weak tache of HPC.
水泥石本体与骨料的界面一直都是混凝土抗裂的薄弱环节。
The content of soluble alkali in cement paste is lower than the optimal one.
水泥中所含可溶碱含量低于最佳可溶碱含量。
Stemming from the washing sieve, a test method of cement paste agglomeration (CPA) was proposed.
由水筛法得到启示，提出了一套水泥净浆结粒的检测方法。
Effect of the above admixtures on strength of mortars and setting of cement paste were measured.
上述外加剂对砂浆强度和水泥凝结时间的影响也是本研究的部分内容。
Mechano electric effect of cement paste under low load to breakage was investigated in this paper.
研究了水泥净浆从小载荷直至破坏时的力电效应。
The technique of the steel tube stake grouted with cement paste is used to consolidate the ground.
采用压浆钢管桩技术加固原有基础，使结构不再继续发生不均匀沉降。
The microstructure of hydrate of cement paste was studied by FTIR reflection spectrum of microscope.
利用红外显微镜反射光谱研究水泥浆体的水化产物微结构。
The molecular weight and sulfonation degree of SPS have little effect on the cement paste properties.
SPS的相对分子质量和磺化度对水泥净浆的性能几乎没有影响。
Light weight aggregate concrete (LWAC) is composed of light weight poriferous aggregate and cement paste.
轻集料混凝土(LWAC)由轻质多孔集料和水泥石胶结而成。
The mechanism of thermal expansion of hydraulic cement paste is also re searched with DSC/TG and XRD methods.
借助于DSC/TG和XRD测试手段，对水泥石的热膨胀性能变化规律进行了机理分析。
In this paper, the test method of the linear thermal expansion coefficient of hardened cement paste is studied.
本文研究了水泥石线性热膨胀系数的测试方法，并针对本试验方法制定了相关的试验制度。
By blending Portland cement and pulverized dehydrated cement paste, a new kink of cementing material is obtained.
把脱水水泥浆与水泥熟料或硅酸盐水泥复合，可以得到一种新型的水硬性胶凝材料。
The water absorption and desorption properties of two shale ceramisites in water and cement paste were investigated.
研究了两种吸水率不同的陶粒在水中和水泥浆中的吸水返水特性。
The effects of five common set-retarders on setting time of cement paste and concrete and strength of concrete are studied.
论文分别研究了木钙、糖钙、酒石酸、焦磷酸钠和蔗糖共五种常用缓凝剂对水泥净浆凝结时间、混凝土凝结时间及强度的影响。
Stirring viscosimeter is employed to research the rheological property of fresh cement paste with different superplasticizers.
用旋转粘度计法研究了掺加不同高效减水剂的新拌水泥浆体的流变性能。
The results indicate that with the increase dosage of fly-ash, the loss of water and drying shrinkage of cement paste increase.
结果表明：随粉煤灰掺量的增加，净浆失水率及干缩率随之增大。
Total porosity of coal gangue cement paste is higher but its pore size at later age is smaller than that of reference cement paste.
与基准水泥浆体相比，煤矸石水泥浆体总孔隙率有所上升，但其孔径后期有所细化。
The retarding properties of cement paste with the super-retarding agent have been characterized and analyzed by means of XRD and SEM.
方法利用XRD和SEM等微观手段，对掺入超缓凝剂水泥砂浆的缓凝性能进行了测试和表征。
A new method of volumetric deformation measurement is proposed, which can measure the shrinkage of cement paste from initial setting.
提出了密封试样细管排液的体积变形测定方法，该方法可测定水泥石自初凝起的收缩。
Flocculated cement structure enclosing lots of water can be found in cement paste, which will influence fluidity and strength of concrete.
新拌水泥浆体中，水泥颗粒互相粘结形成包裹水的絮凝结构，严重影响了混凝土的工作性和强度。
Expansive cement paste and joint concrete are next. And the bond splitting tensile strength of joint surface without bond material is least.
其次是水泥膨浆和接缝混凝土，接缝面不铺筑任何接缝面材料的试块，劈裂抗拉强度最小。